Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.5419 plate,1.5419 Round Bar,1.5419 forgings,1.5419 suppliers, 1.5419 Stock,1.5419 sheet, 1.5419 flat bar, 1.5419 pipe,1.5419 tube,1.5419 mould,1.5419 round ingot,1.5419 cold-rolled steel,1.5419 coil,1.5419 strap steel,1.5419 hot-rolled steel,1.5419 medium plate, 1.5419 heavy plate,1.5419 shapped bar,1.5419 hexahedral bar,1.5419,1.5419 slab ingot,1.5419 slab,1.5419 price,1.5419 square bar,1.5419 square steel,1.5419 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.5419.

Current Location:Home » Products » Alloy steel » 1.5419

Product category

1.5419

Data Table for:Products: Alloy steel:1.5419

1.5419 properties and heat treatment forged piece, Including 1.5419 application and specifications, We have all specifications,Including 1.5419 steel plate, 1.5419 sheet, 1.5419 square steel, 1.5419 flat bar,1.5419 round bar,1.5419 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.5419 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.5419 and Standards

G20Mo5 ( 1.5419 )

  Grade :     G20Mo5
    Number:     1.5419
    Standard: EN 10213 : 2007   steel castings for pressure purposes
EN 10293 : 2005   steel castings for general engineering uses
    Classification:     Ferritic and martensitic

Chemical composition % of the ladle analysis   of grade   G20Mo5 (1.5419)

For casting of ruling thickness < 28 mm, S =< 0.03 % (by mass) is permitted

C Si Mn Ni P S Cr Mo V Cu
0.15 - 0.23 max   0.6 0.5 - 1 max   0.4 max   0.025 max   0.02 max   0.3 0.4 - 0.6 max   0.05 max   0.3

Technological properties of grade   G20Mo5 (1.5419) .

    Welding: ? Preheat temperature from 20 to 200 ? C; ? Interpass temperature max 350 ? C; ? Post Welding heat treatment >= 650 ? C;




Machining performance

Download 1.5419 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.