Our to produce better steel-based products are the main used in industrial manufacturing various types Mould steel20Cr2Ni4 plate,20Cr2Ni4 Round Bar,20Cr2Ni4 forgings,20Cr2Ni4 suppliers, 20Cr2Ni4 Stock,20Cr2Ni4 sheet, 20Cr2Ni4 flat bar, 20Cr2Ni4 pipe,20Cr2Ni4 tube,20Cr2Ni4 mould,20Cr2Ni4 round ingot,20Cr2Ni4 cold-rolled steel,20Cr2Ni4 coil,20Cr2Ni4 strap steel,20Cr2Ni4 hot-rolled steel,20Cr2Ni4 medium plate, 20Cr2Ni4 heavy plate,20Cr2Ni4 shapped bar,20Cr2Ni4 hexahedral bar,20Cr2Ni4,20Cr2Ni4 slab ingot,20Cr2Ni4 slab,20Cr2Ni4 price,20Cr2Ni4 square bar,20Cr2Ni4 square steel,20Cr2Ni4 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 20Cr2Ni4.

Current Location:Home » Products » Mould steel » 20Cr2Ni4

Product category

20Cr2Ni4

Data Table for:Products: Mould steel:20Cr2Ni4

20Cr2Ni4 properties and heat treatment forged piece, Including 20Cr2Ni4 application and specifications, We have all specifications,Including 20Cr2Ni4 steel plate, 20Cr2Ni4 sheet, 20Cr2Ni4 square steel, 20Cr2Ni4 flat bar,20Cr2Ni4 round bar,20Cr2Ni4 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 20Cr2Ni4 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 20Cr2Ni4 and Standards

Step Shaft 20Cr2Ni4 Tube 20Cr2Ni4 Pie-shaped 20Cr2Ni4 Ring 20Cr2Ni4 Module 20Cr2Ni4 Large valves of the main 20Cr2Ni4 Other Profiled Forgings 20Cr2Ni4

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download 20Cr2Ni4 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:20Cr2Ni4 steel plate, 20Cr2Ni4 sheet, 20Cr2Ni4 square steel, 20Cr2Ni4 flat bar,20Cr2Ni4 round bar,20Cr2Ni4 forgings