Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel58CrV4 plate,58CrV4 Round Bar,58CrV4 forgings,58CrV4 suppliers, 58CrV4 Stock,58CrV4 sheet, 58CrV4 flat bar, 58CrV4 pipe,58CrV4 tube,58CrV4 mould,58CrV4 round ingot,58CrV4 cold-rolled steel,58CrV4 coil,58CrV4 strap steel,58CrV4 hot-rolled steel,58CrV4 medium plate, 58CrV4 heavy plate,58CrV4 shapped bar,58CrV4 hexahedral bar,58CrV4,58CrV4 slab ingot,58CrV4 slab,58CrV4 price,58CrV4 square bar,58CrV4 square steel,58CrV4 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 58CrV4.

Current Location:Home » Products » Alloy steel » 58CrV4

Product category

58CrV4

Data Table for:Products: Alloy steel:58CrV4

58CrV4 properties and heat treatment forged piece, Including 58CrV4 application and specifications, We have all specifications,Including 58CrV4 steel plate, 58CrV4 sheet, 58CrV4 square steel, 58CrV4 flat bar,58CrV4 round bar,58CrV4 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 58CrV4 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 58CrV4 and Standards

58CrV4
    DIN-EN Chemical composition
    materials:58CrV4
   materials noW-Nr.: 1.8161
    C(%): 0.55~0.62
    Si(%): 0.15~0.40
    Mn(%): 0.70~1.10
    P(%)≤: 0.035
    S(%)≤: 0.035
    Cr(%): 0.90~1.20
    Mo(%): —
    Ni(%): —
    other(%): V 0.10~0.20
    Heating temperature/°C: 1050~850
    Heating temperature/°C|: 680~720
    Heating temperature/°c: 850~880
 




Machining performance

Download 58CrV4 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.