Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steel80WCrV8 plate,80WCrV8 Round Bar,80WCrV8 forgings,80WCrV8 suppliers, 80WCrV8 Stock,80WCrV8 sheet, 80WCrV8 flat bar, 80WCrV8 pipe,80WCrV8 tube,80WCrV8 mould,80WCrV8 round ingot,80WCrV8 cold-rolled steel,80WCrV8 coil,80WCrV8 strap steel,80WCrV8 hot-rolled steel,80WCrV8 medium plate, 80WCrV8 heavy plate,80WCrV8 shapped bar,80WCrV8 hexahedral bar,80WCrV8,80WCrV8 slab ingot,80WCrV8 slab,80WCrV8 price,80WCrV8 square bar,80WCrV8 square steel,80WCrV8 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 80WCrV8.

Current Location:Home » Products » Tool steel » 80WCrV8

Product category

80WCrV8

Data Table for:Products: Tool steel:80WCrV8

80WCrV8 properties and heat treatment forged piece, Including 80WCrV8 application and specifications, We have all specifications,Including 80WCrV8 steel plate, 80WCrV8 sheet, 80WCrV8 square steel, 80WCrV8 flat bar,80WCrV8 round bar,80WCrV8 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 80WCrV8 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 80WCrV8 and Standards

Si 
Mn 
 P
 S
Cr   Ni  Mo  Other
 0.75-0.85  0.40-0.60  0.30-0.50  0.035  0.035  1.10-1.20      V   0.25-0.35
W   1.80-2.10




Machining performance

Download 80WCrV8 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.