Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelAISI 1019 plate,AISI 1019 Round Bar,AISI 1019 forgings,AISI 1019 suppliers, AISI 1019 Stock,AISI 1019 sheet, AISI 1019 flat bar, AISI 1019 pipe,AISI 1019 tube,AISI 1019 mould,AISI 1019 round ingot,AISI 1019 cold-rolled steel,AISI 1019 coil,AISI 1019 strap steel,AISI 1019 hot-rolled steel,AISI 1019 medium plate, AISI 1019 heavy plate,AISI 1019 shapped bar,AISI 1019 hexahedral bar,AISI 1019,AISI 1019 slab ingot,AISI 1019 slab,AISI 1019 price,AISI 1019 square bar,AISI 1019 square steel,AISI 1019 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 1019.

Current Location:Home » Products » Carbon steel » AISI 1019

Product category

AISI 1019

Data Table for:Products: Carbon steel:AISI 1019

AISI 1019 properties and heat treatment forged piece, Including AISI 1019 application and specifications, We have all specifications,Including AISI 1019 steel plate, AISI 1019 sheet, AISI 1019 square steel, AISI 1019 flat bar,AISI 1019 round bar,AISI 1019 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 1019 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 1019 and Standards

Category  steel
Class  Carbon steel
Type  Standard
Designations  United States: ASTM A29 , ASTM A510 , ASTM A513 , ASTM A519 , ASTM A545 , ASTM A548 , ASTM A576 , SAE J4].2 , SAE J403 , SAE J414 , UNS G10190

Composition
Element Weight %
C  0.15-0.20 
Mn  0.70-1.00 
P  0.04 (max) 
S  0.05 (max)
Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  



Machining performance

Download AISI 1019 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.