Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelAISI 1095 plate,AISI 1095 Round Bar,AISI 1095 forgings,AISI 1095 suppliers, AISI 1095 Stock,AISI 1095 sheet, AISI 1095 flat bar, AISI 1095 pipe,AISI 1095 tube,AISI 1095 mould,AISI 1095 round ingot,AISI 1095 cold-rolled steel,AISI 1095 coil,AISI 1095 strap steel,AISI 1095 hot-rolled steel,AISI 1095 medium plate, AISI 1095 heavy plate,AISI 1095 shapped bar,AISI 1095 hexahedral bar,AISI 1095,AISI 1095 slab ingot,AISI 1095 slab,AISI 1095 price,AISI 1095 square bar,AISI 1095 square steel,AISI 1095 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 1095.

Current Location:Home » Products » Carbon steel » AISI 1095

Product category

AISI 1095

Data Table for:Products: Carbon steel:AISI 1095

AISI 1095 properties and heat treatment forged piece, Including AISI 1095 application and specifications, We have all specifications,Including AISI 1095 steel plate, AISI 1095 sheet, AISI 1095 square steel, AISI 1095 flat bar,AISI 1095 round bar,AISI 1095 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 1095 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 1095 and Standards

Category  steel
Class  Carbon steel
Type  Standard
Designations  Germany: DIN 1.1274
Japan: JIS SUP 4
Sweden: SS 1870
United Kingdom: B.S. 060 A 96 , B.S. En. 44B
United States: AMS 5121 , AMS 5121C , AMS 5122 , AMS 5122C , AMS 5132 , AMS 5132D , AMS 7304 , ASTM A29 , ASTM A510 , ASTM A576 , ASTM A682 , FED QQ-S-700 (1095) , MIL SPEC MIL-S-16788 (C10) , SAE J403 , SAE J412 , SAE J414 , UNS G10950

Composition
Element Weight %
C  0.90-1.03 
Mn  0.30-0.50 
P  0.04 (max) 
S  0.05 (max) 
Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 656.7  25  annealed at 790°C  more
Yield Strength (Mpa) 379.2 
Elongation (%) 13.0 
Reduction in Area (%) 20.6 
Hardness (HB) 192  25  annealed at 790°C more
Impact Strength (J)
(Izod)
2.7  25  annealed at 790°C  more
Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 11.4  0-100 annealed more



Machining performance

Download AISI 1095 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.