Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelAISI A7 plate,AISI A7 Round Bar,AISI A7 forgings,AISI A7 suppliers, AISI A7 Stock,AISI A7 sheet, AISI A7 flat bar, AISI A7 pipe,AISI A7 tube,AISI A7 mould,AISI A7 round ingot,AISI A7 cold-rolled steel,AISI A7 coil,AISI A7 strap steel,AISI A7 hot-rolled steel,AISI A7 medium plate, AISI A7 heavy plate,AISI A7 shapped bar,AISI A7 hexahedral bar,AISI A7,AISI A7 slab ingot,AISI A7 slab,AISI A7 price,AISI A7 square bar,AISI A7 square steel,AISI A7 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI A7.

Current Location:Home » Products » Tool steel » AISI A7

Product category

AISI A7

Data Table for:Products: Tool steel:AISI A7

AISI A7 properties and heat treatment forged piece, Including AISI A7 application and specifications, We have all specifications,Including AISI A7 steel plate, AISI A7 sheet, AISI A7 square steel, AISI A7 flat bar,AISI A7 round bar,AISI A7 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI A7 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI A7 and Standards

Designations 
United States: ASTM A68i , FED QQ-T-570 , UNS T30107

 
Chemical Composition
Element
Weight %
C
 2.00-2.85 
Mn
 0.80 
Si
 0.50 
Cr
 5.00-5.75 
Ni
 0.30 
Mo
 0.90-1.40 
W
 0.50-1.50 
V
 3.90-5.15 
Cu
 0.25 
P
 0.03 
S
 0.03 
 
Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.66
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Thermal Properties
Properties
 Conditions 
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
12.4 
20-425
 



Machining performance

Download AISI A7 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.