Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelAISI L7 plate,AISI L7 Round Bar,AISI L7 forgings,AISI L7 suppliers, AISI L7 Stock,AISI L7 sheet, AISI L7 flat bar, AISI L7 pipe,AISI L7 tube,AISI L7 mould,AISI L7 round ingot,AISI L7 cold-rolled steel,AISI L7 coil,AISI L7 strap steel,AISI L7 hot-rolled steel,AISI L7 medium plate, AISI L7 heavy plate,AISI L7 shapped bar,AISI L7 hexahedral bar,AISI L7,AISI L7 slab ingot,AISI L7 slab,AISI L7 price,AISI L7 square bar,AISI L7 square steel,AISI L7 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI L7.

Current Location:Home » Products » Tool steel » AISI L7

Product category

AISI L7

Data Table for:Products: Tool steel:AISI L7

AISI L7 properties and heat treatment forged piece, Including AISI L7 application and specifications, We have all specifications,Including AISI L7 steel plate, AISI L7 sheet, AISI L7 square steel, AISI L7 flat bar,AISI L7 round bar,AISI L7 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI L7 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI L7 and Standards

C
Si
Mn
P
S
Cr Ni
0.95-1.05 0.2-0.4 0.25-0.45     1.25-1.75  
Mo Al Cu Nb Ti V Ce
0.3-0.5            




Machining performance

Download AISI L7 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:AISI L7 steel plate, AISI L7 sheet, AISI L7 square steel, AISI L7 flat bar,AISI L7 round bar,AISI L7 forgings