Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelAISI M33 plate,AISI M33 Round Bar,AISI M33 forgings,AISI M33 suppliers, AISI M33 Stock,AISI M33 sheet, AISI M33 flat bar, AISI M33 pipe,AISI M33 tube,AISI M33 mould,AISI M33 round ingot,AISI M33 cold-rolled steel,AISI M33 coil,AISI M33 strap steel,AISI M33 hot-rolled steel,AISI M33 medium plate, AISI M33 heavy plate,AISI M33 shapped bar,AISI M33 hexahedral bar,AISI M33,AISI M33 slab ingot,AISI M33 slab,AISI M33 price,AISI M33 square bar,AISI M33 square steel,AISI M33 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI M33.

Current Location:Home » Products » Tool steel » AISI M33

Product category

AISI M33

Data Table for:Products: Tool steel:AISI M33

AISI M33 properties and heat treatment forged piece, Including AISI M33 application and specifications, We have all specifications,Including AISI M33 steel plate, AISI M33 sheet, AISI M33 square steel, AISI M33 flat bar,AISI M33 round bar,AISI M33 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI M33 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI M33 and Standards

Designations
Germany: DIN 1.3249
United Kingdom: B.S. BM 34
United States: ASTM A600 , FED QQ-T-590 , UNS T11333

Chemical Composition
Element
Weight %
C
 0.85-0.92 
Mn
 0.15-0.40 
Si
 0.15-0.50 
Cr
 3.50-4.00 
Ni
 0.3 
Mo
 9.00-10.00 
W
 1.30-2.10 
V
 1.00-1.35 
Co
 7.75-8.75 
Cu
 0.25 
P
 0.03 
S
 0.03 
Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Thermal Properties
Properties
 Conditions 
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
11 
20-425
 



Machining performance

Download AISI M33 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:AISI M33 steel plate, AISI M33 sheet, AISI M33 square steel, AISI M33 flat bar,AISI M33 round bar,AISI M33 forgings