Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelASTM 07 plate,ASTM 07 Round Bar,ASTM 07 forgings,ASTM 07 suppliers, ASTM 07 Stock,ASTM 07 sheet, ASTM 07 flat bar, ASTM 07 pipe,ASTM 07 tube,ASTM 07 mould,ASTM 07 round ingot,ASTM 07 cold-rolled steel,ASTM 07 coil,ASTM 07 strap steel,ASTM 07 hot-rolled steel,ASTM 07 medium plate, ASTM 07 heavy plate,ASTM 07 shapped bar,ASTM 07 hexahedral bar,ASTM 07,ASTM 07 slab ingot,ASTM 07 slab,ASTM 07 price,ASTM 07 square bar,ASTM 07 square steel,ASTM 07 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 07.

Current Location:Home » Products » Tool steel » ASTM 07

Product category


Data Table for:Products: Tool steel:ASTM 07

ASTM 07 properties and heat treatment forged piece, Including ASTM 07 application and specifications, We have all specifications,Including ASTM 07 steel plate, ASTM 07 sheet, ASTM 07 square steel, ASTM 07 flat bar,ASTM 07 round bar,ASTM 07 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM 07 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM 07 and Standards

Cr Ni
1.1-1.3 0.1-0.6 0.2-1.0  0.03  0.03 0.35-0.85  
Mo Al W Nb Ti V Ce
≤0.3    1.0-2.0     0.15-0.4   

Machining performance

Download ASTM 07 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.