Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelASTM 51310 plate,ASTM 51310 Round Bar,ASTM 51310 forgings,ASTM 51310 suppliers, ASTM 51310 Stock,ASTM 51310 sheet, ASTM 51310 flat bar, ASTM 51310 pipe,ASTM 51310 tube,ASTM 51310 mould,ASTM 51310 round ingot,ASTM 51310 cold-rolled steel,ASTM 51310 coil,ASTM 51310 strap steel,ASTM 51310 hot-rolled steel,ASTM 51310 medium plate, ASTM 51310 heavy plate,ASTM 51310 shapped bar,ASTM 51310 hexahedral bar,ASTM 51310,ASTM 51310 slab ingot,ASTM 51310 slab,ASTM 51310 price,ASTM 51310 square bar,ASTM 51310 square steel,ASTM 51310 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 51310.

Current Location:Home » Products » Alloy steel » ASTM 51310

Product category

ASTM 51310

Data Table for:Products: Alloy steel:ASTM 51310

ASTM 51310 properties and heat treatment forged piece, Including ASTM 51310 application and specifications, We have all specifications,Including ASTM 51310 steel plate, ASTM 51310 sheet, ASTM 51310 square steel, ASTM 51310 flat bar,ASTM 51310 round bar,ASTM 51310 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM 51310 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM 51310 and Standards

C :0.32~0.39
Si:0.17~0.37
Mn:0.50~0.80
S :≤0.035
P :≤0.035
Cr:0.80~1.10

 

CHINA GB USA  ASTM JAPAN JISG Germany DIN UK   BS     NF ISO
35Cr 51310 SCr435 34Cr4 34Cr4 34Cr4 34Cr4




Machining performance

Download ASTM 51310 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM 51310 steel plate, ASTM 51310 sheet, ASTM 51310 square steel, ASTM 51310 flat bar,ASTM 51310 round bar,ASTM 51310 forgings