Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelASTM A2 plate,ASTM A2 Round Bar,ASTM A2 forgings,ASTM A2 suppliers, ASTM A2 Stock,ASTM A2 sheet, ASTM A2 flat bar, ASTM A2 pipe,ASTM A2 tube,ASTM A2 mould,ASTM A2 round ingot,ASTM A2 cold-rolled steel,ASTM A2 coil,ASTM A2 strap steel,ASTM A2 hot-rolled steel,ASTM A2 medium plate, ASTM A2 heavy plate,ASTM A2 shapped bar,ASTM A2 hexahedral bar,ASTM A2,ASTM A2 slab ingot,ASTM A2 slab,ASTM A2 price,ASTM A2 square bar,ASTM A2 square steel,ASTM A2 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A2.

Current Location:Home » Products » Tool steel » ASTM A2

Product category


Data Table for:Products: Tool steel:ASTM A2

ASTM A2 properties and heat treatment forged piece, Including ASTM A2 application and specifications, We have all specifications,Including ASTM A2 steel plate, ASTM A2 sheet, ASTM A2 square steel, ASTM A2 flat bar,ASTM A2 round bar,ASTM A2 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM A2 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM A2 and Standards

Cr Ni
0.95-1.05   0.1-0.5  0.4-1.0 0.03  0.03   4.75-5.5  
Mo Al Cu Nb Ti V Ce
 0.9-1.4         0.15-0.5   

Machining performance

Download ASTM A2 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:ASTM A2 steel plate, ASTM A2 sheet, ASTM A2 square steel, ASTM A2 flat bar,ASTM A2 round bar,ASTM A2 forgings