Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelASTM A8 plate,ASTM A8 Round Bar,ASTM A8 forgings,ASTM A8 suppliers, ASTM A8 Stock,ASTM A8 sheet, ASTM A8 flat bar, ASTM A8 pipe,ASTM A8 tube,ASTM A8 mould,ASTM A8 round ingot,ASTM A8 cold-rolled steel,ASTM A8 coil,ASTM A8 strap steel,ASTM A8 hot-rolled steel,ASTM A8 medium plate, ASTM A8 heavy plate,ASTM A8 shapped bar,ASTM A8 hexahedral bar,ASTM A8,ASTM A8 slab ingot,ASTM A8 slab,ASTM A8 price,ASTM A8 square bar,ASTM A8 square steel,ASTM A8 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A8.

Current Location:Home » Products » Tool steel » ASTM A8

Product category


Data Table for:Products: Tool steel:ASTM A8

ASTM A8 properties and heat treatment forged piece, Including ASTM A8 application and specifications, We have all specifications,Including ASTM A8 steel plate, ASTM A8 sheet, ASTM A8 square steel, ASTM A8 flat bar,ASTM A8 round bar,ASTM A8 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM A8 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM A8 and Standards

Cr Ni
0.5-0.6  0.75-1.1 0.2-0.5 0.03  0.03  4.75-5.5  
Mo Al W Nb Ti V Ce
1.15-1.65   1.0-1.5         

Machining performance

Download ASTM A8 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:ASTM A8 steel plate, ASTM A8 sheet, ASTM A8 square steel, ASTM A8 flat bar,ASTM A8 round bar,ASTM A8 forgings