Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelAlgotuf 50R plate,Algotuf 50R Round Bar,Algotuf 50R forgings,Algotuf 50R suppliers, Algotuf 50R Stock,Algotuf 50R sheet, Algotuf 50R flat bar, Algotuf 50R pipe,Algotuf 50R tube,Algotuf 50R mould,Algotuf 50R round ingot,Algotuf 50R cold-rolled steel,Algotuf 50R coil,Algotuf 50R strap steel,Algotuf 50R hot-rolled steel,Algotuf 50R medium plate, Algotuf 50R heavy plate,Algotuf 50R shapped bar,Algotuf 50R hexahedral bar,Algotuf 50R,Algotuf 50R slab ingot,Algotuf 50R slab,Algotuf 50R price,Algotuf 50R square bar,Algotuf 50R square steel,Algotuf 50R wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Algotuf 50R.

Current Location:Home » Products » Carbon steel » Algotuf 50R

Product category

Algotuf 50R

Data Table for:Products: Carbon steel:Algotuf 50R

Algotuf 50R properties and heat treatment forged piece, Including Algotuf 50R application and specifications, We have all specifications,Including Algotuf 50R steel plate, Algotuf 50R sheet, Algotuf 50R square steel, Algotuf 50R flat bar,Algotuf 50R round bar,Algotuf 50R forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Algotuf 50R has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Algotuf 50R and Standards

C(%):    0.16
Si(%):    0.75
Mn(%):    0.75
Cr(%):    0.30~1.25
Ni(%):    0.90
Cu(%):    0.20~0.60

P 0.075~0.15




Machining performance

Download Algotuf 50R the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.