Our to produce better steel-based products are the main used in industrial manufacturing various types Cementation steelsC10GPb plate,C10GPb Round Bar,C10GPb forgings,C10GPb suppliers, C10GPb Stock,C10GPb sheet, C10GPb flat bar, C10GPb pipe,C10GPb tube,C10GPb mould,C10GPb round ingot,C10GPb cold-rolled steel,C10GPb coil,C10GPb strap steel,C10GPb hot-rolled steel,C10GPb medium plate, C10GPb heavy plate,C10GPb shapped bar,C10GPb hexahedral bar,C10GPb,C10GPb slab ingot,C10GPb slab,C10GPb price,C10GPb square bar,C10GPb square steel,C10GPb wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of C10GPb.

Current Location:Home » Products » Cementation steels » C10GPb

Product category

C10GPb

Data Table for:Products: Cementation steels:C10GPb

C10GPb properties and heat treatment forged piece, Including C10GPb application and specifications, We have all specifications,Including C10GPb steel plate, C10GPb sheet, C10GPb square steel, C10GPb flat bar,C10GPb round bar,C10GPb forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the C10GPb has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade C10GPb and Standards

Material number 1.0302 - C10Pb / C10GPb
Composition in % :

C
Si
Mn
P
S
Cr
Mo
Ni
0,06 - 0,12
0,15 - 0,35
0,25 - 0,50
max. 0,045
max. 0,045
 
 
 

 
 

V
W
Ti
Cu
Al
Nb
B
Pb
 
 
 
 
 
 
 
0,15 - 0,30

Range of application and heat treatment :

Cementation steel / Free-cutting steel : for structural- and machine components - pins , boxes , lever
Hardening : 880 - 920 °C (water) Soft annealing : 650 - 700 °C
 

General and distinctive features :

 




Machining performance

Download C10GPb the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:C10GPb steel plate, C10GPb sheet, C10GPb square steel, C10GPb flat bar,C10GPb round bar,C10GPb forgings