Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelFTi70S08 plate,FTi70S08 Round Bar,FTi70S08 forgings,FTi70S08 suppliers, FTi70S08 Stock,FTi70S08 sheet, FTi70S08 flat bar, FTi70S08 pipe,FTi70S08 tube,FTi70S08 mould,FTi70S08 round ingot,FTi70S08 cold-rolled steel,FTi70S08 coil,FTi70S08 strap steel,FTi70S08 hot-rolled steel,FTi70S08 medium plate, FTi70S08 heavy plate,FTi70S08 shapped bar,FTi70S08 hexahedral bar,FTi70S08,FTi70S08 slab ingot,FTi70S08 slab,FTi70S08 price,FTi70S08 square bar,FTi70S08 square steel,FTi70S08 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of FTi70S08.

Current Location:Home » Products » Carbon steel » FTi70S08

Product category

FTi70S08

Data Table for:Products: Carbon steel:FTi70S08

FTi70S08 properties and heat treatment forged piece, Including FTi70S08 application and specifications, We have all specifications,Including FTi70S08 steel plate, FTi70S08 sheet, FTi70S08 square steel, FTi70S08 flat bar,FTi70S08 round bar,FTi70S08 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the FTi70S08 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade FTi70S08 and Standards

C Si Mn S P Cr Mo V Ti Al Cu Zr Sn
max 0.3 max 0.8 max 0.8 max 0.03 max 0.03 max 0.8 max 2 max 1.8 68 - 75 max 4 max 0.3 max 1.5 max 0.15




Machining performance

Download FTi70S08 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:FTi70S08 steel plate, FTi70S08 sheet, FTi70S08 square steel, FTi70S08 flat bar,FTi70S08 round bar,FTi70S08 forgings