Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelFeMn90C01LP plate,FeMn90C01LP Round Bar,FeMn90C01LP forgings,FeMn90C01LP suppliers, FeMn90C01LP Stock,FeMn90C01LP sheet, FeMn90C01LP flat bar, FeMn90C01LP pipe,FeMn90C01LP tube,FeMn90C01LP mould,FeMn90C01LP round ingot,FeMn90C01LP cold-rolled steel,FeMn90C01LP coil,FeMn90C01LP strap steel,FeMn90C01LP hot-rolled steel,FeMn90C01LP medium plate, FeMn90C01LP heavy plate,FeMn90C01LP shapped bar,FeMn90C01LP hexahedral bar,FeMn90C01LP,FeMn90C01LP slab ingot,FeMn90C01LP slab,FeMn90C01LP price,FeMn90C01LP square bar,FeMn90C01LP square steel,FeMn90C01LP wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of FeMn90C01LP.

Current Location:Home » Products » Carbon steel » FeMn90C01LP

Product category

FeMn90C01LP

Data Table for:Products: Carbon steel:FeMn90C01LP

FeMn90C01LP properties and heat treatment forged piece, Including FeMn90C01LP application and specifications, We have all specifications,Including FeMn90C01LP steel plate, FeMn90C01LP sheet, FeMn90C01LP square steel, FeMn90C01LP flat bar,FeMn90C01LP round bar,FeMn90C01LP forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the FeMn90C01LP has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade FeMn90C01LP and Standards

C Si Mn S P
max 0.1 max 2 85 - 95 max 0.03 max 0.15




Machining performance

Download FeMn90C01LP the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:FeMn90C01LP steel plate, FeMn90C01LP sheet, FeMn90C01LP square steel, FeMn90C01LP flat bar,FeMn90C01LP round bar,FeMn90C01LP forgings