Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelFeMnSi28LP plate,FeMnSi28LP Round Bar,FeMnSi28LP forgings,FeMnSi28LP suppliers, FeMnSi28LP Stock,FeMnSi28LP sheet, FeMnSi28LP flat bar, FeMnSi28LP pipe,FeMnSi28LP tube,FeMnSi28LP mould,FeMnSi28LP round ingot,FeMnSi28LP cold-rolled steel,FeMnSi28LP coil,FeMnSi28LP strap steel,FeMnSi28LP hot-rolled steel,FeMnSi28LP medium plate, FeMnSi28LP heavy plate,FeMnSi28LP shapped bar,FeMnSi28LP hexahedral bar,FeMnSi28LP,FeMnSi28LP slab ingot,FeMnSi28LP slab,FeMnSi28LP price,FeMnSi28LP square bar,FeMnSi28LP square steel,FeMnSi28LP wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of FeMnSi28LP.

Current Location:Home » Products » Carbon steel » FeMnSi28LP

Product category

FeMnSi28LP

Data Table for:Products: Carbon steel:FeMnSi28LP

FeMnSi28LP properties and heat treatment forged piece, Including FeMnSi28LP application and specifications, We have all specifications,Including FeMnSi28LP steel plate, FeMnSi28LP sheet, FeMnSi28LP square steel, FeMnSi28LP flat bar,FeMnSi28LP round bar,FeMnSi28LP forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the FeMnSi28LP has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade FeMnSi28LP and Standards

C Si Mn S P
max 0.5 25 - 30 65 - 75 max 0.03 max 0.1




Machining performance

Download FeMnSi28LP the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:FeMnSi28LP steel plate, FeMnSi28LP sheet, FeMnSi28LP square steel, FeMnSi28LP flat bar,FeMnSi28LP round bar,FeMnSi28LP forgings