Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelFeMnSi30LP plate,FeMnSi30LP Round Bar,FeMnSi30LP forgings,FeMnSi30LP suppliers, FeMnSi30LP Stock,FeMnSi30LP sheet, FeMnSi30LP flat bar, FeMnSi30LP pipe,FeMnSi30LP tube,FeMnSi30LP mould,FeMnSi30LP round ingot,FeMnSi30LP cold-rolled steel,FeMnSi30LP coil,FeMnSi30LP strap steel,FeMnSi30LP hot-rolled steel,FeMnSi30LP medium plate, FeMnSi30LP heavy plate,FeMnSi30LP shapped bar,FeMnSi30LP hexahedral bar,FeMnSi30LP,FeMnSi30LP slab ingot,FeMnSi30LP slab,FeMnSi30LP price,FeMnSi30LP square bar,FeMnSi30LP square steel,FeMnSi30LP wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of FeMnSi30LP.

Current Location:Home » Products » Carbon steel » FeMnSi30LP

Product category

FeMnSi30LP

Data Table for:Products: Carbon steel:FeMnSi30LP

FeMnSi30LP properties and heat treatment forged piece, Including FeMnSi30LP application and specifications, We have all specifications,Including FeMnSi30LP steel plate, FeMnSi30LP sheet, FeMnSi30LP square steel, FeMnSi30LP flat bar,FeMnSi30LP round bar,FeMnSi30LP forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the FeMnSi30LP has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade FeMnSi30LP and Standards

C Si Mn S P
max 0.1 28 - 35 57 - 67 max 0.03 max 0.1




Machining performance

Download FeMnSi30LP the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:FeMnSi30LP steel plate, FeMnSi30LP sheet, FeMnSi30LP square steel, FeMnSi30LP flat bar,FeMnSi30LP round bar,FeMnSi30LP forgings