Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelFeV80A114 plate,FeV80A114 Round Bar,FeV80A114 forgings,FeV80A114 suppliers, FeV80A114 Stock,FeV80A114 sheet, FeV80A114 flat bar, FeV80A114 pipe,FeV80A114 tube,FeV80A114 mould,FeV80A114 round ingot,FeV80A114 cold-rolled steel,FeV80A114 coil,FeV80A114 strap steel,FeV80A114 hot-rolled steel,FeV80A114 medium plate, FeV80A114 heavy plate,FeV80A114 shapped bar,FeV80A114 hexahedral bar,FeV80A114,FeV80A114 slab ingot,FeV80A114 slab,FeV80A114 price,FeV80A114 square bar,FeV80A114 square steel,FeV80A114 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of FeV80A114.

Current Location:Home » Products » Carbon steel » FeV80A114

Product category

FeV80A114

Data Table for:Products: Carbon steel:FeV80A114

FeV80A114 properties and heat treatment forged piece, Including FeV80A114 application and specifications, We have all specifications,Including FeV80A114 steel plate, FeV80A114 sheet, FeV80A114 square steel, FeV80A114 flat bar,FeV80A114 round bar,FeV80A114 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the FeV80A114 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade FeV80A114 and Standards

C Si Mn Ni S P V Al Cu As
max 0.2 max 2 max 0.5 max 0.15 max 0.1 max 0.1 70 - 80 max 4 max 0.1 max 0.1




Machining performance

Download FeV80A114 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:FeV80A114 steel plate, FeV80A114 sheet, FeV80A114 square steel, FeV80A114 flat bar,FeV80A114 round bar,FeV80A114 forgings