Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloyHaynes 188 plate,Haynes 188 Round Bar,Haynes 188 forgings,Haynes 188 suppliers, Haynes 188 Stock,Haynes 188 sheet, Haynes 188 flat bar, Haynes 188 pipe,Haynes 188 tube,Haynes 188 mould,Haynes 188 round ingot,Haynes 188 cold-rolled steel,Haynes 188 coil,Haynes 188 strap steel,Haynes 188 hot-rolled steel,Haynes 188 medium plate, Haynes 188 heavy plate,Haynes 188 shapped bar,Haynes 188 hexahedral bar,Haynes 188,Haynes 188 slab ingot,Haynes 188 slab,Haynes 188 price,Haynes 188 square bar,Haynes 188 square steel,Haynes 188 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Haynes 188.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » Haynes 188

Product category

Haynes 188

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:Haynes 188

Haynes 188 properties and heat treatment forged piece, Including Haynes 188 application and specifications, We have all specifications,Including Haynes 188 steel plate, Haynes 188 sheet, Haynes 188 square steel, Haynes 188 flat bar,Haynes 188 round bar,Haynes 188 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Haynes 188 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Haynes 188 and Standards

Principal Design Features
This is a cobalt-nickel-chromium-tungsten alloy designed for high temperature strength and resistance to oxidation at temperatures up to 2000 F(1095 C).

request for quote

Applications
While primarily employed in the aerospace industry, this alloy has found uses in commercial industrial applications including land-based gas turbines. Generally found in hot sections of engines in burner cans, ducting and afterburner components. In recent years, it has been eclipsed by Alloy 230 for many applications due to improved properties.

Machinability
Conventional machining techniques used for iron based alloys may be used. This alloy does work-harden during machining and has higher strength and "gumminess" not typical of steels. Heavy duty machining equipment and tooling should be used to minimize chatter or work-hardening of the alloy ahead of the cutting.
 




Machining performance

Download Haynes 188 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.