Our to produce better steel-based products are the main used in industrial manufacturing various types Heat resistant steelN08825 plate,N08825 Round Bar,N08825 forgings,N08825 suppliers, N08825 Stock,N08825 sheet, N08825 flat bar, N08825 pipe,N08825 tube,N08825 mould,N08825 round ingot,N08825 cold-rolled steel,N08825 coil,N08825 strap steel,N08825 hot-rolled steel,N08825 medium plate, N08825 heavy plate,N08825 shapped bar,N08825 hexahedral bar,N08825,N08825 slab ingot,N08825 slab,N08825 price,N08825 square bar,N08825 square steel,N08825 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of N08825.

Current Location:Home » Products » Heat resistant steel » N08825

Product category

N08825

Data Table for:Products: Heat resistant steel:N08825

N08825 properties and heat treatment forged piece, Including N08825 application and specifications, We have all specifications,Including N08825 steel plate, N08825 sheet, N08825 square steel, N08825 flat bar,N08825 round bar,N08825 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the N08825 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade N08825 and Standards

Grade :   KHN32T   ( ХН32Т ) (   Х20Н32Т     ЭП670   )
      Classification :   Hidh-temperature or heat-resistant alloy
      Equivalent steels:  
Chemical composition in % for grade   KHN32T   ( ХН32Т ) GOST   5632 - 72
Fe C Si Mn Ni S P Cr Ti Al
41.4 - 50.75 max   0.05 max   0.7 max   0.7 30 - 34 max   0.02 max   0.03 19 - 22 0.25 - 0.6 max   0.5

Mechanical properties under Т=20oС for grade   KHN32T   ( ХН32Т ) "
Assortment Dimension Direct. sв sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
Bar   longitudinal 480 180 40 60   Heating 1100 - 1150oC,Cooling air,
Sheet   dihedral 500 180 30     Heating 1080oC,Cooling water,
Forging     470 176 30 35    

Physical properties for grade   KHN32T   ( ХН32Т )
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m
20 2.05   15.9 8160    
100   13.7 13.4      
200   15.6 15.1      
300   17.2 16.7      
400   18 18      
500   18 19.2      
600   18.4 20.5      
700   18.9 21.7      
800   19 23.4      
T E 10- 5 a 10 6 l r C R 10 9

Equivalent steels for grade   KHN32T   ( ХН32Т )
USA Germany Japan France England European Spain Romania South Korea
- DIN,WNr JIS AFNOR BS EN UNE STAS KS
N08825
UNSNo8800
UNSNo8810
X10NiCrAlTi32-20
X2NiCrAiTi32-20
X5NiCrAlTi31-20
X8NiCrAlTi32-21
NCF2HTF
NCF800
NCF800TB
Z10NC32-21
Z8NC33-21
NA15
NA15H
X10NiCrAlTi32-21
X10NiCrAlTi32-20
X10NiCrAlTi32-20
X10NiCrAlTi32-21
X3CrMnNiN18-8-7
10TiAlCrNi320
NCF800

Specification :
Mechanical properties :
sв - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]




Machining performance

Download N08825 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.