Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelSAE 3135 plate,SAE 3135 Round Bar,SAE 3135 forgings,SAE 3135 suppliers, SAE 3135 Stock,SAE 3135 sheet, SAE 3135 flat bar, SAE 3135 pipe,SAE 3135 tube,SAE 3135 mould,SAE 3135 round ingot,SAE 3135 cold-rolled steel,SAE 3135 coil,SAE 3135 strap steel,SAE 3135 hot-rolled steel,SAE 3135 medium plate, SAE 3135 heavy plate,SAE 3135 shapped bar,SAE 3135 hexahedral bar,SAE 3135,SAE 3135 slab ingot,SAE 3135 slab,SAE 3135 price,SAE 3135 square bar,SAE 3135 square steel,SAE 3135 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of SAE 3135.

Current Location:Home » Products » Carbon steel » SAE 3135

Product category

SAE 3135

Data Table for:Products: Carbon steel:SAE 3135

SAE 3135 properties and heat treatment forged piece, Including SAE 3135 application and specifications, We have all specifications,Including SAE 3135 steel plate, SAE 3135 sheet, SAE 3135 square steel, SAE 3135 flat bar,SAE 3135 round bar,SAE 3135 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the SAE 3135 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade SAE 3135 and Standards

 C(%):    0.33~0.38

Si(%):    0.20~0.35
Mn(%):    0.60~0.80
P(%)≤:    0.040
S(%)≤:    0.040
Cr(%):    0.55~0.75
Ni(%):    1.10~1.40



Machining performance

Download SAE 3135 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:SAE 3135 steel plate, SAE 3135 sheet, SAE 3135 square steel, SAE 3135 flat bar,SAE 3135 round bar,SAE 3135 forgings