Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S44023 plate,UNS S44023 Round Bar,UNS S44023 forgings,UNS S44023 suppliers, UNS S44023 Stock,UNS S44023 sheet, UNS S44023 flat bar, UNS S44023 pipe,UNS S44023 tube,UNS S44023 mould,UNS S44023 round ingot,UNS S44023 cold-rolled steel,UNS S44023 coil,UNS S44023 strap steel,UNS S44023 hot-rolled steel,UNS S44023 medium plate, UNS S44023 heavy plate,UNS S44023 shapped bar,UNS S44023 hexahedral bar,UNS S44023,UNS S44023 slab ingot,UNS S44023 slab,UNS S44023 price,UNS S44023 square bar,UNS S44023 square steel,UNS S44023 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S44023.

Current Location:Home » Products » Stainless Steel » UNS S44023

Product category

UNS S44023

Data Table for:Products: Stainless Steel:UNS S44023

UNS S44023 properties and heat treatment forged piece, Including UNS S44023 application and specifications, We have all specifications,Including UNS S44023 steel plate, UNS S44023 sheet, UNS S44023 square steel, UNS S44023 flat bar,UNS S44023 round bar,UNS S44023 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS S44023 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS S44023 and Standards

 C(%): 0.95~1.20
Si(%): ≤1.00
Mn(%): ≤1.25
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 16.0~18.0
Ni(%): ≤0.75
Mo(%): ≤0.60
Se≥0.15




Machining performance

Download UNS S44023 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.