Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelUNS T13107 plate,UNS T13107 Round Bar,UNS T13107 forgings,UNS T13107 suppliers, UNS T13107 Stock,UNS T13107 sheet, UNS T13107 flat bar, UNS T13107 pipe,UNS T13107 tube,UNS T13107 mould,UNS T13107 round ingot,UNS T13107 cold-rolled steel,UNS T13107 coil,UNS T13107 strap steel,UNS T13107 hot-rolled steel,UNS T13107 medium plate, UNS T13107 heavy plate,UNS T13107 shapped bar,UNS T13107 hexahedral bar,UNS T13107,UNS T13107 slab ingot,UNS T13107 slab,UNS T13107 price,UNS T13107 square bar,UNS T13107 square steel,UNS T13107 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS T13107.

Current Location:Home » Products » Tool steel » UNS T13107

Product category

UNS T13107

Data Table for:Products: Tool steel:UNS T13107

UNS T13107 properties and heat treatment forged piece, Including UNS T13107 application and specifications, We have all specifications,Including UNS T13107 steel plate, UNS T13107 sheet, UNS T13107 square steel, UNS T13107 flat bar,UNS T13107 round bar,UNS T13107 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the UNS T13107 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade UNS T13107 and Standards

Cr Ni
0.97-1.05 0.2-0.55 0.15-0.4 0.03 0.03 3.5-4  
Mo Al W Nb Ti V Ce
8.2-9.2   1.4-2.1     1.75-2.25  

Machining performance

Download UNS T13107 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.