Chemical composition % of the ladle analysis of grade 40SiNiCr250

C(％) Si(％) Mn(％) P(％) S(％) Cr(％) Ni(％) Mo(％) W(%) Cu(%)
0. 30-0. 50 1.00-2.50 0. 50-1.50 0. 045 0.030 24.0-26.0 19.0-21.0 0. 20 0. 40-0.60 0. 30
40SiNiCr250
Mechanical properties of grade 40SiNiCr250
Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
741 (≥) 646 (≥) 41 31 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 133
Physical properties of grade 40SiNiCr250
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
491 (≥) 764 (≥) 44 22 14 Solution and Aging, Annealing, Ausaging, Q+T,etc 231
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
445 746 992
40SiNiCr250 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Enquiry