Martensite Stainless Steels Z12CNDV12-03, Z12CNDV12.03, Z12CNDV12.03, X12CrNiMoV12.3, 1.4938, Iron and steel. Stainless steel for high temperature application to EN 10269:1999

Z12CNDV12-03 Stainless Steels Properties Data

Chemical Composition of steel Z12CNDV12-03 Stainless Steels: EN 10269:1999 ,Cross Reference

Z12CNDV12-03 Stainless Steels Applications and Specifications

Z 12 CNDV 12-03 is a new type of martensitic stainless steel for the last-stage blades of large-capacity nuclear and thermal power turbines. The deformation behavior of this steel was studied by thermal compression experiments that performed on a Gleeble-3500 thermal simulator at a temperature range of 850°C to 1200°C and a strain rate of 0.01s-1 to 20s-1. When the deformation was performed at high temperature and low strain rate, a necklace type of microstructures was observed, the plastic deformation mechanism is grain boundary slip and migration, when at low temperature and lower strain rate, the slip bands were observed, the mechanism is intracrystalline slips, and when at strain rate of 20s-1, twins were observed, the mechanism are slips and twins. The Arrhenius equation was applied to describe the constitutive equation of the flow stress. The accuracy of the equation was verified by using the experimental data and the correlation coefficient R2 = 0.9786, and the equation can provide reasonable data for the design and numerical simulation of the Z12CNDV12-03 forging process.

  • EN 10269:1999 - Steels and nickel alloys for fasteners with specified elevated and/or low temperature propertiesture application
  • NF A35-578 - Iron and steel. Stainless steel for high temperature application

Mechanical properties at room temperature for Z12CNDV12-03 Stainless Steels: EN 10269:1999

Tensile Strength,Rm(MPa)

Yield Strength,Rp 0.2(MPa)

Impact,Kv/Ku(J)

Elongation,A(%)

Reduction of area,(%)

Hardness

Product shapes we supply:

Cross Reference, Equivalent, Similar of Z12CNDV12-03 Stainless Steels grade:

Z12CNDV12-03 Z12CNDV12-03 X12CrNiMoV12-3 1.4938

Conditions & Properties

  • +A Soft annealed
  • +AC Annealed to achieve spheroidization of the carbides
  • +QT Quenched and tempered
  • +WW Warm worked
  • +N Normalized
  • +NT Normalized and tempered
  • +AT Solution annealed
  • +C Cold drawn / Hard
  • +CR Cold rolled
  • +PE Peeled
  • +T Tempered