Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.4306 plate,1.4306 Round Bar,1.4306 forgings,1.4306 suppliers, 1.4306 Stock,1.4306 sheet, 1.4306 flat bar, 1.4306 pipe,1.4306 tube,1.4306 mould,1.4306 round ingot,1.4306 cold-rolled steel,1.4306 coil,1.4306 strap steel,1.4306 hot-rolled steel,1.4306 medium plate, 1.4306 heavy plate,1.4306 shapped bar,1.4306 hexahedral bar,1.4306,1.4306 slab ingot,1.4306 slab,1.4306 price,1.4306 square bar,1.4306 square steel,1.4306 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.4306.

Current Location:Home » Products » Alloy steel » 1.4306

Product category

1.4306

Data Table for:Products: Alloy steel:1.4306

1.4306 properties and heat treatment forged piece, Including 1.4306 application and specifications, We have all specifications,Including 1.4306 steel plate, 1.4306 sheet, 1.4306 square steel, 1.4306 flat bar,1.4306 round bar,1.4306 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.4306 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.4306 and Standards

X2CrNi19-11   ( 1.4306 )

Grade :     X2CrNi19-11
    Number:     1.4306
    Standard: EN 10088 - 2 : 2005   stainless steels. Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
EN 10088 - 3 : 2005   stainless steels. Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
    Classification:     Austenitic stainless steels - Standard grade

Chemical composition % of the ladle analysis   of grade   X2CrNi19-11 (1.4306)

Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended.
Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
 

C Si Mn Ni P S Cr N
max   0.03 max   1 max   2 10 - 12 max   0.045 max   0.015 18 - 20 max   0.11

Equivalent grades of grade   X2CrNi19-11 (1.4306)

USA
-
Japan
JIS
France
AFNOR
England
BS
Sweden
SS
Poland
PN
Finland
SFS
Russia
GOST
304L
SUS304L
Z3CN18-10
304S11
2352
00H18N10
720
03KH18N11




Machining performance

Download 1.4306 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:1.4306 steel plate, 1.4306 sheet, 1.4306 square steel, 1.4306 flat bar,1.4306 round bar,1.4306 forgings