Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.4876 plate,1.4876 Round Bar,1.4876 forgings,1.4876 suppliers, 1.4876 Stock,1.4876 sheet, 1.4876 flat bar, 1.4876 pipe,1.4876 tube,1.4876 mould,1.4876 round ingot,1.4876 cold-rolled steel,1.4876 coil,1.4876 strap steel,1.4876 hot-rolled steel,1.4876 medium plate, 1.4876 heavy plate,1.4876 shapped bar,1.4876 hexahedral bar,1.4876,1.4876 slab ingot,1.4876 slab,1.4876 price,1.4876 square bar,1.4876 square steel,1.4876 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.4876.

Current Location:Home » Products » Alloy steel » 1.4876

Product category

1.4876

Data Table for:Products: Alloy steel:1.4876

1.4876 properties and heat treatment forged piece, Including 1.4876 application and specifications, We have all specifications,Including 1.4876 steel plate, 1.4876 sheet, 1.4876 square steel, 1.4876 flat bar,1.4876 round bar,1.4876 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.4876 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.4876 and Standards

X10NiCrAlTi32-21 ( 1.4876 )

    Grade :     X10NiCrAlTi32-21
    Number:     1.4876
    Standard: EN 10095 : 1999   Heat Resisting steels and Nickel Alloys
    Classification:     Austenitic heat-resisting steels

Chemical composition % of the ladle analysis   of grade   X10NiCrAlTi32-21 (1.4876)

C Si Mn Ni P S Cr Ti Al
max   0.12 max   1 max   2 30 - 34 max   0.03 max   0.015 19 - 23 0.15 - 0.6 0.15 - 0.6




Machining performance

Download 1.4876 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.