Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel1.6570 plate,1.6570 Round Bar,1.6570 forgings,1.6570 suppliers, 1.6570 Stock,1.6570 sheet, 1.6570 flat bar, 1.6570 pipe,1.6570 tube,1.6570 mould,1.6570 round ingot,1.6570 cold-rolled steel,1.6570 coil,1.6570 strap steel,1.6570 hot-rolled steel,1.6570 medium plate, 1.6570 heavy plate,1.6570 shapped bar,1.6570 hexahedral bar,1.6570,1.6570 slab ingot,1.6570 slab,1.6570 price,1.6570 square bar,1.6570 square steel,1.6570 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.6570.

Current Location:Home » Products » Alloy steel » 1.6570

Product category

1.6570

Data Table for:Products: Alloy steel:1.6570

1.6570 properties and heat treatment forged piece, Including 1.6570 application and specifications, We have all specifications,Including 1.6570 steel plate, 1.6570 sheet, 1.6570 square steel, 1.6570 flat bar,1.6570 round bar,1.6570 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.6570 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.6570 and Standards

G32NiCrMo8-5-4   ( 1.6570 )

Grade :     G32NiCrMo8-5-4
    Number:     1.6570
    Standard: EN 10293 : 2005   steel castings for general engineering uses
    Classification:     steel castings for general engineering uses

Chemical composition % of the ladle analysis   of grade   G32NiCrMo8-5-4 (1.6570)

C Si Mn Ni P S Cr Mo
0.28 - 0.35 max   0.6 0.6 - 1 1.6 - 2.1 max   0.02 max   0.015 1 - 1.4 0.3 - 0.5

Technological properties of grade   G32NiCrMo8-5-4 (1.6570) .

    Welding: ? Preheat temperature from 200 to 350 ? C; ? Interpass temperature max 400 ? C; ? Post Welding heat treatment >= 560 ? C;




Machining performance

Download 1.6570 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.