Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel2.4856 plate,2.4856 Round Bar,2.4856 forgings,2.4856 suppliers, 2.4856 Stock,2.4856 sheet, 2.4856 flat bar, 2.4856 pipe,2.4856 tube,2.4856 mould,2.4856 round ingot,2.4856 cold-rolled steel,2.4856 coil,2.4856 strap steel,2.4856 hot-rolled steel,2.4856 medium plate, 2.4856 heavy plate,2.4856 shapped bar,2.4856 hexahedral bar,2.4856,2.4856 slab ingot,2.4856 slab,2.4856 price,2.4856 square bar,2.4856 square steel,2.4856 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 2.4856.

Current Location:Home » Products » Alloy steel » 2.4856

Product category

2.4856

Data Table for:Products: Alloy steel:2.4856

2.4856 properties and heat treatment forged piece, Including 2.4856 application and specifications, We have all specifications,Including 2.4856 steel plate, 2.4856 sheet, 2.4856 square steel, 2.4856 flat bar,2.4856 round bar,2.4856 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 2.4856 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 2.4856 and Standards

NiCr22Mo9Nb ( 2.4856 )

Grade :     NiCr22Mo9Nb
    Number:     2.4856
    Standard: EN 10095 : 1999   Heat Resisting steels and Nickel Alloys
    Classification:     Austenitic nickel alloy

Chemical composition % of the ladle analysis   of grade   NiCr22Mo9Nb (2.4856)

Ni -rest
Nb + Ta = 3.15 - 4.15

Fe C Si Mn Ni P S Cr Mo Co Ti Al Cu
max   5 0.03 - 0.1 max   0.5 max   0.5 max   58 max   0.02 max   0.015 20 - 23 8 - 10 max   1 max   0.4 max   0.4 max   0.5




Machining performance

Download 2.4856 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:2.4856 steel plate, 2.4856 sheet, 2.4856 square steel, 2.4856 flat bar,2.4856 round bar,2.4856 forgings