Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steel2.4889 plate,2.4889 Round Bar,2.4889 forgings,2.4889 suppliers, 2.4889 Stock,2.4889 sheet, 2.4889 flat bar, 2.4889 pipe,2.4889 tube,2.4889 mould,2.4889 round ingot,2.4889 cold-rolled steel,2.4889 coil,2.4889 strap steel,2.4889 hot-rolled steel,2.4889 medium plate, 2.4889 heavy plate,2.4889 shapped bar,2.4889 hexahedral bar,2.4889,2.4889 slab ingot,2.4889 slab,2.4889 price,2.4889 square bar,2.4889 square steel,2.4889 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 2.4889.

Current Location:Home » Products » Alloy steel » 2.4889

Product category

2.4889

Data Table for:Products: Alloy steel:2.4889

2.4889 properties and heat treatment forged piece, Including 2.4889 application and specifications, We have all specifications,Including 2.4889 steel plate, 2.4889 sheet, 2.4889 square steel, 2.4889 flat bar,2.4889 round bar,2.4889 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 2.4889 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 2.4889 and Standards

NiCr28FeSiCe ( 2.4889 )

  Grade :     NiCr28FeSiCe
    Number:     2.4889
    Standard: EN 10095 : 1999   Heat Resisting steels and Nickel Alloys
    Classification:     Austenitic nickel alloy

Chemical composition % of the ladle analysis   of grade   NiCr28FeSiCe (2.4889)

Ni - rest
A maximum of 1.5% Co is allowed and counted as nickel. Reporting of cobalt is not requred.

Fe Si Mn Ni P S Cr Ce Cu
21 - 25 2.5 - 3 max   1 max   45 max   0.02 max   0.01 26 - 29 0.03 - 0.09 max   0.3




Machining performance

Download 2.4889 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.