Our to produce better steel-based products are the main used in industrial manufacturing various types Ti Alloy3.7035 plate,3.7035 Round Bar,3.7035 forgings,3.7035 suppliers, 3.7035 Stock,3.7035 sheet, 3.7035 flat bar, 3.7035 pipe,3.7035 tube,3.7035 mould,3.7035 round ingot,3.7035 cold-rolled steel,3.7035 coil,3.7035 strap steel,3.7035 hot-rolled steel,3.7035 medium plate, 3.7035 heavy plate,3.7035 shapped bar,3.7035 hexahedral bar,3.7035,3.7035 slab ingot,3.7035 slab,3.7035 price,3.7035 square bar,3.7035 square steel,3.7035 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 3.7035.

Current Location:Home » Products » Ti Alloy » 3.7035

Product category

3.7035

Data Table for:Products: Ti Alloy:3.7035

3.7035 properties and heat treatment forged piece, Including 3.7035 application and specifications, We have all specifications,Including 3.7035 steel plate, 3.7035 sheet, 3.7035 square steel, 3.7035 flat bar,3.7035 round bar,3.7035 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 3.7035 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 3.7035 and Standards

3.7035

Material No. 3.7035
EN symbol (short) Ti-II
AISI/SAE
UNS R 50400
AFNOR
B.S.
Alloy
Registered work's label Ti 994-Ti-grade2
Standards DIN 17850

 

Description

Our product range in 3.7025 are tubes and pipes, fittings and flanges, accessories

Chemical composition

C
≤%
N
≤%
H
≤%
Fe
≤%
O
≤%
Pa
%
Others
%
Ti
 
0,08 0,06 0,013 0,25 0,20   0,4 rest

Special characteristics

Temperature range Density kg/dm³ Hardness HB
  approx. 4,5  
particularly good stability against corrosion, low specific weight, little cold-straining

Welding filler

Welding rod and wire electrode SG-Ti2

Main fields of application (depending on the specific conditions of use)

chemical industry, offshore platforms, aviation, space travel, highly stressed weight-saving components, condensers, sea water desalination plants, power stations




Machining performance

Download 3.7035 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:3.7035 steel plate, 3.7035 sheet, 3.7035 square steel, 3.7035 flat bar,3.7035 round bar,3.7035 forgings