Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelAISI 1117 plate,AISI 1117 Round Bar,AISI 1117 forgings,AISI 1117 suppliers, AISI 1117 Stock,AISI 1117 sheet, AISI 1117 flat bar, AISI 1117 pipe,AISI 1117 tube,AISI 1117 mould,AISI 1117 round ingot,AISI 1117 cold-rolled steel,AISI 1117 coil,AISI 1117 strap steel,AISI 1117 hot-rolled steel,AISI 1117 medium plate, AISI 1117 heavy plate,AISI 1117 shapped bar,AISI 1117 hexahedral bar,AISI 1117,AISI 1117 slab ingot,AISI 1117 slab,AISI 1117 price,AISI 1117 square bar,AISI 1117 square steel,AISI 1117 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 1117.

Current Location:Home » Products » Carbon steel » AISI 1117

Product category

AISI 1117

Data Table for:Products: Carbon steel:AISI 1117

AISI 1117 properties and heat treatment forged piece, Including AISI 1117 application and specifications, We have all specifications,Including AISI 1117 steel plate, AISI 1117 sheet, AISI 1117 square steel, AISI 1117 flat bar,AISI 1117 round bar,AISI 1117 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 1117 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 1117 and Standards

Category  steel
Class  Carbon steel
Type  Standard resulfurized
Designations  United States: AMS 5022G , ASTM A107 , ASTM A108 , FED QQ-S-637 (1117) , MIL SPEC MIL-S-18411 , SAE J403 , SAE J412 , SAE J414 , UNS G11170

Composition
Element Weight %
C  0.14-0.20 
Mn  1.00-1.30 
P  0.04 (max) 
S  0.08-0.13 
Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 429.5  25  annealed at 855°C  more
Yield Strength (Mpa) 279.2 
Elongation (%) 32.8 
Reduction in Area (%) 58.0 
Hardness (HB) 121  25  annealed at 855°C more
Impact Strength (J)
(Izod)
93.6  25  annealed at 855°C  more



Machining performance

Download AISI 1117 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.