Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelAISI 4330 plate,AISI 4330 Round Bar,AISI 4330 forgings,AISI 4330 suppliers, AISI 4330 Stock,AISI 4330 sheet, AISI 4330 flat bar, AISI 4330 pipe,AISI 4330 tube,AISI 4330 mould,AISI 4330 round ingot,AISI 4330 cold-rolled steel,AISI 4330 coil,AISI 4330 strap steel,AISI 4330 hot-rolled steel,AISI 4330 medium plate, AISI 4330 heavy plate,AISI 4330 shapped bar,AISI 4330 hexahedral bar,AISI 4330,AISI 4330 slab ingot,AISI 4330 slab,AISI 4330 price,AISI 4330 square bar,AISI 4330 square steel,AISI 4330 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 4330.

Current Location:Home » Products » Alloy steel » AISI 4330

Product category

AISI 4330

Data Table for:Products: Alloy steel:AISI 4330

AISI 4330 properties and heat treatment forged piece, Including AISI 4330 application and specifications, We have all specifications,Including AISI 4330 steel plate, AISI 4330 sheet, AISI 4330 square steel, AISI 4330 flat bar,AISI 4330 round bar,AISI 4330 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 4330 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 4330 and Standards

MetalTek MTEK J24054 4330 Alloy Steel
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel

Material Notes: Alloys for general structural use.
Applications: Cylinders, rolls, hollow shafts.

Information provided by MetalTek

Cast UNS J24054; Cast Grade 10B; Cast ASTM A487; AMS 5328b; Wrought UNS ; Wrought Grade AISI 4330

Mechanical Properties Metric English Comments
Hardness, Brinell  285 285
Tensile Strength, Ultimate  >= 860 MPa >= 125000 psi
Tensile Strength, Yield  >= 690 MPa >= 100000 psi
Elongation at Break  >= 15.0 % >= 15.0 %
 
Component Elements Properties Metric English Comments
Carbon, C  0.20 - 0.30 % 0.20 - 0.30 %
Chromium, Cr  0.40 - 0.60 % 0.40 - 0.60 %
Iron, Fe  95.3 - 98.1 % 95.3 - 98.1 %
Manganese, Mn  <= 1.0 % <= 1.0 %
Molybdenum, Mo  0.30 - 0.50 % 0.30 - 0.50 %
Nickel, Ni  1.0 - 1.50 % 1.0 - 1.50 %
Silicon, Si  <= 0.80 % <= 0.80 %
 
Descriptive Properties
Heat Treatment Quench & Temper

Users viewing this material also viewed the following:
Latrobe Lescalloy® 4330+V VAC-ARC High Strength Alloy Steel
Latrobe Lescalloy® 4335+V VAC-ARC High Strength Alloy Steel
AISI 4145 steel
MetalTek MTEK J13345 4130 Alloy Steel
AISI 4340 steel, annealed, 25 mm round

NMETEK117 / 18367
 




Machining performance

Download AISI 4330 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:AISI 4330 steel plate, AISI 4330 sheet, AISI 4330 square steel, AISI 4330 flat bar,AISI 4330 round bar,AISI 4330 forgings