Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelAISI 4817 plate,AISI 4817 Round Bar,AISI 4817 forgings,AISI 4817 suppliers, AISI 4817 Stock,AISI 4817 sheet, AISI 4817 flat bar, AISI 4817 pipe,AISI 4817 tube,AISI 4817 mould,AISI 4817 round ingot,AISI 4817 cold-rolled steel,AISI 4817 coil,AISI 4817 strap steel,AISI 4817 hot-rolled steel,AISI 4817 medium plate, AISI 4817 heavy plate,AISI 4817 shapped bar,AISI 4817 hexahedral bar,AISI 4817,AISI 4817 slab ingot,AISI 4817 slab,AISI 4817 price,AISI 4817 square bar,AISI 4817 square steel,AISI 4817 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 4817.

Current Location:Home » Products » Alloy steel » AISI 4817

Product category

AISI 4817

Data Table for:Products: Alloy steel:AISI 4817

AISI 4817 properties and heat treatment forged piece, Including AISI 4817 application and specifications, We have all specifications,Including AISI 4817 steel plate, AISI 4817 sheet, AISI 4817 square steel, AISI 4817 flat bar,AISI 4817 round bar,AISI 4817 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 4817 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 4817 and Standards

AISI 4817 steel
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel; Low Alloy Steel; Carbon Steel; Low Carbon steel

Key Words: UNS G48170, ASTM A304, ASTM A322, ASTM A331, ASTM A519, SAE J404, SAE J412, SAE J770, low carbon steels

Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell  187 - 229 187 - 229 hot rolled and cold drawn.
Hardness, Knoop  230 230 Converted from Brinell hardness.
Hardness, Rockwell B  94 94 Converted from Brinell hardness.
Hardness, Rockwell C  15.0 15.0 Converted from Brinell hardness. Value below normal HRC range, for comparison purposes only.
Hardness, Vickers  218 218 Converted from Brinell hardness.
Modulus of Elasticity  205 GPa 29700 ksi Typical for steel
Compressive Yield Strength  1795 MPa 260300 psi 1585 MPa mean, gears with case depth 1.1 to 1.5 mm, 60 HRC min. case hardness.
Bulk Modulus  140 GPa 20300 ksi Typical for steel.
Poissons Ratio  0.290 0.290 Calculated
Machinability  60 % 60 % hot rolled and cold drawn. Based on 100% machinability for AISI 1212 steel.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000245 ohm-cm 0.0000245 ohm-cm Typical 4000 series steel
 
Thermal Properties Metric English Comments
Specific Heat Capacity  0.475 J/g-°C 0.114 BTU/lb-°F Typical 4000 series steel
Thermal Conductivity  44.5 W/m-K 309 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Carbon, C  0.150 - 0.200 % 0.150 - 0.200 %
Iron, Fe  94.775 - 95.85 % 94.775 - 95.85 % As remainder
Manganese, Mn  0.400 - 0.600 % 0.400 - 0.600 %
Molybdenum, Mo  0.200 - 0.300 % 0.200 - 0.300 %
Nickel, Ni  3.25 - 3.75 % 3.25 - 3.75 %
Phosphorous, P  <= 0.0350 % <= 0.0350 %
Silicon, Si  0.150 - 0.300 % 0.150 - 0.300 %
Sulfur, S  <= 0.0400 % <= 0.0400 %

Users viewing this material also viewed the following:
AISI 4720 Steel
AISI 4820 Steel, annealed 815°C (1500°F)
AISI 4615 Steel
AISI 4815 Steel, pseudocarburized, reheated to 775°C (1430°F) and oil quenched, 150°C (300°F) temper, 25 mm (1 in.) round
AISI 4626 Steel

M481BA / 7968
 




Machining performance

Download AISI 4817 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.