Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelAISI L5 plate,AISI L5 Round Bar,AISI L5 forgings,AISI L5 suppliers, AISI L5 Stock,AISI L5 sheet, AISI L5 flat bar, AISI L5 pipe,AISI L5 tube,AISI L5 mould,AISI L5 round ingot,AISI L5 cold-rolled steel,AISI L5 coil,AISI L5 strap steel,AISI L5 hot-rolled steel,AISI L5 medium plate, AISI L5 heavy plate,AISI L5 shapped bar,AISI L5 hexahedral bar,AISI L5,AISI L5 slab ingot,AISI L5 slab,AISI L5 price,AISI L5 square bar,AISI L5 square steel,AISI L5 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI L5.

Current Location:Home » Products » Tool steel » AISI L5

Product category


Data Table for:Products: Tool steel:AISI L5

AISI L5 properties and heat treatment forged piece, Including AISI L5 application and specifications, We have all specifications,Including AISI L5 steel plate, AISI L5 sheet, AISI L5 square steel, AISI L5 flat bar,AISI L5 round bar,AISI L5 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the AISI L5 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade AISI L5 and Standards

Cr Ni
0.9-1.1 0.1-0.4 0.9-1.1     0.9-1.1  
Mo Al Cu Nb Ti V Ce

Machining performance

Download AISI L5 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:AISI L5 steel plate, AISI L5 sheet, AISI L5 square steel, AISI L5 flat bar,AISI L5 round bar,AISI L5 forgings