Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelASTM 9Q plate,ASTM 9Q Round Bar,ASTM 9Q forgings,ASTM 9Q suppliers, ASTM 9Q Stock,ASTM 9Q sheet, ASTM 9Q flat bar, ASTM 9Q pipe,ASTM 9Q tube,ASTM 9Q mould,ASTM 9Q round ingot,ASTM 9Q cold-rolled steel,ASTM 9Q coil,ASTM 9Q strap steel,ASTM 9Q hot-rolled steel,ASTM 9Q medium plate, ASTM 9Q heavy plate,ASTM 9Q shapped bar,ASTM 9Q hexahedral bar,ASTM 9Q,ASTM 9Q slab ingot,ASTM 9Q slab,ASTM 9Q price,ASTM 9Q square bar,ASTM 9Q square steel,ASTM 9Q wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM 9Q.

Current Location:Home » Products » Alloy steel » ASTM 9Q

Product category

ASTM 9Q

Data Table for:Products: Alloy steel:ASTM 9Q

ASTM 9Q properties and heat treatment forged piece, Including ASTM 9Q application and specifications, We have all specifications,Including ASTM 9Q steel plate, ASTM 9Q sheet, ASTM 9Q square steel, ASTM 9Q flat bar,ASTM 9Q round bar,ASTM 9Q forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM 9Q has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM 9Q and Standards

C
Si
Mn
P
S
Cr Ni
0.25-0.35 0.2-0.8 0.4-0.7 0.04 0.045 0.7-0.9 1.65-2.0
Mo Al Cu Nb Ti W Ce
0.2-0.3   0.5     0.1  




Machining performance

Download ASTM 9Q the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM 9Q steel plate, ASTM 9Q sheet, ASTM 9Q square steel, ASTM 9Q flat bar,ASTM 9Q round bar,ASTM 9Q forgings