Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelASTM CN3MN plate,ASTM CN3MN Round Bar,ASTM CN3MN forgings,ASTM CN3MN suppliers, ASTM CN3MN Stock,ASTM CN3MN sheet, ASTM CN3MN flat bar, ASTM CN3MN pipe,ASTM CN3MN tube,ASTM CN3MN mould,ASTM CN3MN round ingot,ASTM CN3MN cold-rolled steel,ASTM CN3MN coil,ASTM CN3MN strap steel,ASTM CN3MN hot-rolled steel,ASTM CN3MN medium plate, ASTM CN3MN heavy plate,ASTM CN3MN shapped bar,ASTM CN3MN hexahedral bar,ASTM CN3MN,ASTM CN3MN slab ingot,ASTM CN3MN slab,ASTM CN3MN price,ASTM CN3MN square bar,ASTM CN3MN square steel,ASTM CN3MN wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM CN3MN.

Current Location:Home » Products » Alloy steel » ASTM CN3MN

Product category

ASTM CN3MN

Data Table for:Products: Alloy steel:ASTM CN3MN

ASTM CN3MN properties and heat treatment forged piece, Including ASTM CN3MN application and specifications, We have all specifications,Including ASTM CN3MN steel plate, ASTM CN3MN sheet, ASTM CN3MN square steel, ASTM CN3MN flat bar,ASTM CN3MN round bar,ASTM CN3MN forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM CN3MN has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM CN3MN and Standards

C
Si
Mn
P
S
Cr Ni
0.03 1.0 2.0 0.04 0.04 20.0-22.0 23.5-25.5
Mo Al Cu Nb Ti V Ce
6.0-7.0   ≤0.75        
N Co Pb B Other    
0.18-0.26            




Machining performance

Download ASTM CN3MN the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.