Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelASTM W210 plate,ASTM W210 Round Bar,ASTM W210 forgings,ASTM W210 suppliers, ASTM W210 Stock,ASTM W210 sheet, ASTM W210 flat bar, ASTM W210 pipe,ASTM W210 tube,ASTM W210 mould,ASTM W210 round ingot,ASTM W210 cold-rolled steel,ASTM W210 coil,ASTM W210 strap steel,ASTM W210 hot-rolled steel,ASTM W210 medium plate, ASTM W210 heavy plate,ASTM W210 shapped bar,ASTM W210 hexahedral bar,ASTM W210,ASTM W210 slab ingot,ASTM W210 slab,ASTM W210 price,ASTM W210 square bar,ASTM W210 square steel,ASTM W210 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM W210.

Current Location:Home » Products » Tool steel » ASTM W210

Product category


Data Table for:Products: Tool steel:ASTM W210

ASTM W210 properties and heat treatment forged piece, Including ASTM W210 application and specifications, We have all specifications,Including ASTM W210 steel plate, ASTM W210 sheet, ASTM W210 square steel, ASTM W210 flat bar,ASTM W210 round bar,ASTM W210 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the ASTM W210 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade ASTM W210 and Standards

Cr Ni
0.95-1.1  0.1-0.4  0.1-0.4 0.025  0.025     
Mo Al Cu Nb Ti V Ce

Machining performance

Download ASTM W210 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:ASTM W210 steel plate, ASTM W210 sheet, ASTM W210 square steel, ASTM W210 flat bar,ASTM W210 round bar,ASTM W210 forgings