Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelC55E plate,C55E Round Bar,C55E forgings,C55E suppliers, C55E Stock,C55E sheet, C55E flat bar, C55E pipe,C55E tube,C55E mould,C55E round ingot,C55E cold-rolled steel,C55E coil,C55E strap steel,C55E hot-rolled steel,C55E medium plate, C55E heavy plate,C55E shapped bar,C55E hexahedral bar,C55E,C55E slab ingot,C55E slab,C55E price,C55E square bar,C55E square steel,C55E wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of C55E.

Current Location:Home » Products » Alloy steel » C55E

Product category

C55E

Data Table for:Products: Alloy steel:C55E

C55E properties and heat treatment forged piece, Including C55E application and specifications, We have all specifications,Including C55E steel plate, C55E sheet, C55E square steel, C55E flat bar,C55E round bar,C55E forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the C55E has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade C55E and Standards

C55E   ( 1.1203 )

 

Chemical composition % of the ladle analysis   of grade   C55E (1.1203)
Cr + Mo + Ni = max 0.63

    Grade :     C55E     Number:     1.1203     Standard: EN 10083 - 2 : 2006   steels for quenching and tempering. Technical delivery conditions for non alloy steels
EN 10132 - 3 : 2000   Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. steels for quenching and tempering     Classification:     Special steel

Equivalent grades of grade   C55E (1.1203)
Germany
DIN,WNr
France
AFNOR
England
BS
Italy
UNI
Spain
UNE
Russia
GOST
International
ISO
Ck55
XC55H1
070M55
C55
C55k
F1150
55
C55E4

C Si Mn Ni P S Cr Mo 0.52 - 0.6 max   0.4 0.6 - 0.9 max   0.4 max   0.03 max   0.035 max   0.4 max   0.1




Machining performance

Download C55E the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.