Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyDIN 1.0909 plate,DIN 1.0909 Round Bar,DIN 1.0909 forgings,DIN 1.0909 suppliers, DIN 1.0909 Stock,DIN 1.0909 sheet, DIN 1.0909 flat bar, DIN 1.0909 pipe,DIN 1.0909 tube,DIN 1.0909 mould,DIN 1.0909 round ingot,DIN 1.0909 cold-rolled steel,DIN 1.0909 coil,DIN 1.0909 strap steel,DIN 1.0909 hot-rolled steel,DIN 1.0909 medium plate, DIN 1.0909 heavy plate,DIN 1.0909 shapped bar,DIN 1.0909 hexahedral bar,DIN 1.0909,DIN 1.0909 slab ingot,DIN 1.0909 slab,DIN 1.0909 price,DIN 1.0909 square bar,DIN 1.0909 square steel,DIN 1.0909 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of DIN 1.0909.

Current Location:Home » Products » Ti Alloy » DIN 1.0909

Product category

DIN 1.0909

Data Table for:Products: Ti Alloy:DIN 1.0909

DIN 1.0909 properties and heat treatment forged piece, Including DIN 1.0909 application and specifications, We have all specifications,Including DIN 1.0909 steel plate, DIN 1.0909 sheet, DIN 1.0909 square steel, DIN 1.0909 flat bar,DIN 1.0909 round bar,DIN 1.0909 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the DIN 1.0909 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade DIN 1.0909 and Standards

Category  steel
Class  Alloy steel
Type  Standard
Common Names  Silicon-manganese steel
Designations  France: AFNOR 60 S 7 , AFNOR 61 SC 7
Germany: DIN 1.0909
United Kingdom: B.S. 250 A 58
United States: ASTM A29 , ASTM A322 , ASTM A331 , ASTM A505 , ASTM A519 , ASTM A59 , SAE J1268 , SAE J404 , SAE J412 , SAE J770 , UNS G92600

Composition
Element Weight %
C  0.56-0.64 
Mn  0.75-1.00 
P  0.035 (max) 
S  0.04 (max) 
Si  1.80-2.20 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1758  25  oil quenched, fine grained, tempered at 425°C  more
Yield Strength (Mpa) 1503 
Elongation (%)
Reduction in Area (%) 24 
Hardness (HB) 600  25  oil quenched, fine grained, tempered at 205°C more




Machining performance

Download DIN 1.0909 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:DIN 1.0909 steel plate, DIN 1.0909 sheet, DIN 1.0909 square steel, DIN 1.0909 flat bar,DIN 1.0909 round bar,DIN 1.0909 forgings