Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelFeMn80C01 plate,FeMn80C01 Round Bar,FeMn80C01 forgings,FeMn80C01 suppliers, FeMn80C01 Stock,FeMn80C01 sheet, FeMn80C01 flat bar, FeMn80C01 pipe,FeMn80C01 tube,FeMn80C01 mould,FeMn80C01 round ingot,FeMn80C01 cold-rolled steel,FeMn80C01 coil,FeMn80C01 strap steel,FeMn80C01 hot-rolled steel,FeMn80C01 medium plate, FeMn80C01 heavy plate,FeMn80C01 shapped bar,FeMn80C01 hexahedral bar,FeMn80C01,FeMn80C01 slab ingot,FeMn80C01 slab,FeMn80C01 price,FeMn80C01 square bar,FeMn80C01 square steel,FeMn80C01 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of FeMn80C01.

Current Location:Home » Products » Carbon steel » FeMn80C01

Product category

FeMn80C01

Data Table for:Products: Carbon steel:FeMn80C01

FeMn80C01 properties and heat treatment forged piece, Including FeMn80C01 application and specifications, We have all specifications,Including FeMn80C01 steel plate, FeMn80C01 sheet, FeMn80C01 square steel, FeMn80C01 flat bar,FeMn80C01 round bar,FeMn80C01 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the FeMn80C01 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade FeMn80C01 and Standards

C Si Mn S P
max 0.1 max 2 75 - 85 max 0.03 max 0.3




Machining performance

Download FeMn80C01 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:FeMn80C01 steel plate, FeMn80C01 sheet, FeMn80C01 square steel, FeMn80C01 flat bar,FeMn80C01 round bar,FeMn80C01 forgings