Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyHM21A-T81 plate,HM21A-T81 Round Bar,HM21A-T81 forgings,HM21A-T81 suppliers, HM21A-T81 Stock,HM21A-T81 sheet, HM21A-T81 flat bar, HM21A-T81 pipe,HM21A-T81 tube,HM21A-T81 mould,HM21A-T81 round ingot,HM21A-T81 cold-rolled steel,HM21A-T81 coil,HM21A-T81 strap steel,HM21A-T81 hot-rolled steel,HM21A-T81 medium plate, HM21A-T81 heavy plate,HM21A-T81 shapped bar,HM21A-T81 hexahedral bar,HM21A-T81,HM21A-T81 slab ingot,HM21A-T81 slab,HM21A-T81 price,HM21A-T81 square bar,HM21A-T81 square steel,HM21A-T81 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of HM21A-T81.

Current Location:Home » Products » Ti Alloy » HM21A-T81

Product category

HM21A-T81

Data Table for:Products: Ti Alloy:HM21A-T81

HM21A-T81 properties and heat treatment forged piece, Including HM21A-T81 application and specifications, We have all specifications,Including HM21A-T81 steel plate, HM21A-T81 sheet, HM21A-T81 square steel, HM21A-T81 flat bar,HM21A-T81 round bar,HM21A-T81 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the HM21A-T81 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade HM21A-T81 and Standards

Physical Properties Metric English Comments
Density  1.78 g/cc 0.0643 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate  255 MPa 37000 psi
Tensile Strength, Yield  210 MPa 30500 psi
Elongation at Break  6.00 % 6.00 % in 50 mm
Modulus of Elasticity  45.0 GPa 6530 ksi In Tension
Compressive Yield Strength  180 MPa 26100 psi
Notched Tensile Strength  260 MPa 37700 psi 60° V-Notch, root radius 0.0076 mm.
Ultimate Bearing Strength  455 MPa 66000 psi
Bearing Yield Strength  320 MPa 46400 psi
Poissons Ratio  0.350 0.350
Machinability  100 % 100 % Relative Rating, 100=Best
Shear Modulus  17.0 GPa 2470 ksi
Shear Strength  170 MPa 24700 psi
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.00000500 ohm-cm 0.00000500 ohm-cm
 
Thermal Properties Metric English Comments
Heat of Fusion  343 J/g 148 BTU/lb
CTE, linear 26.8 µm/m-°C
@Temperature 0.000 - 100 °C
14.9 µin/in-°F
@Temperature 32.0 - 212 °F
  27.0 µm/m-°C
@Temperature 20.0 - 200 °C
15.0 µin/in-°F
@Temperature 68.0 - 392 °F
Estimated from similar Mg alloys
Specific Heat Capacity  1.00 J/g-°C 0.239 BTU/lb-°F
Thermal Conductivity  135 W/m-K 937 BTU-in/hr-ft²-°F Estimated from trends in similar Mg alloys.
Melting Point  605 - 650 °C 1120 - 1200 °F
Solidus  605 °C 1120 °F
Liquidus  650 °C 1200 °F
 
Processing Properties Metric English Comments
Processing Temperature  455 - 595 °C 851 - 1100 °F Hot Working
Annealing Temperature  455 °C 851 °F
 
Component Elements Properties Metric English Comments
Magnesium, Mg  97.0 % 97.0 % As Remainder
Manganese, Mn  0.45 - 1.10 % 0.45 - 1.10 %
Thorium, Th  1.50 - 2.50 % 1.50 - 2.50 %




Machining performance

Download HM21A-T81 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.