Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelNiCr23Fe plate,NiCr23Fe Round Bar,NiCr23Fe forgings,NiCr23Fe suppliers, NiCr23Fe Stock,NiCr23Fe sheet, NiCr23Fe flat bar, NiCr23Fe pipe,NiCr23Fe tube,NiCr23Fe mould,NiCr23Fe round ingot,NiCr23Fe cold-rolled steel,NiCr23Fe coil,NiCr23Fe strap steel,NiCr23Fe hot-rolled steel,NiCr23Fe medium plate, NiCr23Fe heavy plate,NiCr23Fe shapped bar,NiCr23Fe hexahedral bar,NiCr23Fe,NiCr23Fe slab ingot,NiCr23Fe slab,NiCr23Fe price,NiCr23Fe square bar,NiCr23Fe square steel,NiCr23Fe wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of NiCr23Fe.

Current Location:Home » Products » Alloy steel » NiCr23Fe

Product category

NiCr23Fe

Data Table for:Products: Alloy steel:NiCr23Fe

NiCr23Fe properties and heat treatment forged piece, Including NiCr23Fe application and specifications, We have all specifications,Including NiCr23Fe steel plate, NiCr23Fe sheet, NiCr23Fe square steel, NiCr23Fe flat bar,NiCr23Fe round bar,NiCr23Fe forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the NiCr23Fe has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade NiCr23Fe and Standards

NiCr23Fe ( 2.4851 )

Grade :     NiCr23Fe
    Number:     2.4851
    Standard: EN 10095 : 1999   Heat Resisting steels and Nickel Alloys
    Classification:     Austenitic nickel alloy

Chemical composition % of the ladle analysis   of grade   NiCr23Fe (2.4851)

A maximum of 1.5% Co is allowed and counted as nickel. Reporting of cobalt is not requred.

Fe C Si Mn Ni P S Cr Ti Al Cu B
max   18 0.03 - 0.1 max   0.5 max   1 58 - 63 max   0.02 max   0.015 21 - 25 max   0.5 1 - 1.7 max   0.5 max   0.006

 




Machining performance

Download NiCr23Fe the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.