Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-6Al-6V-2Sn-0.75Cu plate,Ti-6Al-6V-2Sn-0.75Cu Round Bar,Ti-6Al-6V-2Sn-0.75Cu forgings,Ti-6Al-6V-2Sn-0.75Cu suppliers, Ti-6Al-6V-2Sn-0.75Cu Stock,Ti-6Al-6V-2Sn-0.75Cu sheet, Ti-6Al-6V-2Sn-0.75Cu flat bar, Ti-6Al-6V-2Sn-0.75Cu pipe,Ti-6Al-6V-2Sn-0.75Cu tube,Ti-6Al-6V-2Sn-0.75Cu mould,Ti-6Al-6V-2Sn-0.75Cu round ingot,Ti-6Al-6V-2Sn-0.75Cu cold-rolled steel,Ti-6Al-6V-2Sn-0.75Cu coil,Ti-6Al-6V-2Sn-0.75Cu strap steel,Ti-6Al-6V-2Sn-0.75Cu hot-rolled steel,Ti-6Al-6V-2Sn-0.75Cu medium plate, Ti-6Al-6V-2Sn-0.75Cu heavy plate,Ti-6Al-6V-2Sn-0.75Cu shapped bar,Ti-6Al-6V-2Sn-0.75Cu hexahedral bar,Ti-6Al-6V-2Sn-0.75Cu,Ti-6Al-6V-2Sn-0.75Cu slab ingot,Ti-6Al-6V-2Sn-0.75Cu slab,Ti-6Al-6V-2Sn-0.75Cu price,Ti-6Al-6V-2Sn-0.75Cu square bar,Ti-6Al-6V-2Sn-0.75Cu square steel,Ti-6Al-6V-2Sn-0.75Cu wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-6Al-6V-2Sn-0.75Cu.

Current Location:Home » Products » Ti Alloy » Ti-6Al-6V-2Sn-0.75Cu

Product category

Ti-6Al-6V-2Sn-0.75Cu

Data Table for:Products: Ti Alloy:Ti-6Al-6V-2Sn-0.75Cu

Ti-6Al-6V-2Sn-0.75Cu properties and heat treatment forged piece, Including Ti-6Al-6V-2Sn-0.75Cu application and specifications, We have all specifications,Including Ti-6Al-6V-2Sn-0.75Cu steel plate, Ti-6Al-6V-2Sn-0.75Cu sheet, Ti-6Al-6V-2Sn-0.75Cu square steel, Ti-6Al-6V-2Sn-0.75Cu flat bar,Ti-6Al-6V-2Sn-0.75Cu round bar,Ti-6Al-6V-2Sn-0.75Cu forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-6Al-6V-2Sn-0.75Cu has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-6Al-6V-2Sn-0.75Cu and Standards

Category  Titanium Alloy
Class  Wrought
Type  Alpha-beta alloy
Designations  United States: MIL-T-9046, AMS 4971, AMS 4918, MIL-T-9047, AMS 4978, AMS 4979

Composition
Element Weight %
Al  6 
V  6 
Sn  2 
Cu  0.75 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 4.54 25  
Poisson's Ratio 0.33 25  
Elastic Modulus (GPa) 110.3 25  
Tensile Strength (Mpa) 1069  25  annealed  more
Yield Strength (Mpa) 1000 
Elongation (%) 14 
Reduction in Area (%) 30 
Hardness (HRC) 38  25  annealed more
Impact Strength (J)
(Charpy)
18  25  annealed  

Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 9  20-100 more  




Machining performance

Download Ti-6Al-6V-2Sn-0.75Cu the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-6Al-6V-2Sn-0.75Cu steel plate, Ti-6Al-6V-2Sn-0.75Cu sheet, Ti-6Al-6V-2Sn-0.75Cu square steel, Ti-6Al-6V-2Sn-0.75Cu flat bar,Ti-6Al-6V-2Sn-0.75Cu round bar,Ti-6Al-6V-2Sn-0.75Cu forgings