Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelUNS G50401 plate,UNS G50401 Round Bar,UNS G50401 forgings,UNS G50401 suppliers, UNS G50401 Stock,UNS G50401 sheet, UNS G50401 flat bar, UNS G50401 pipe,UNS G50401 tube,UNS G50401 mould,UNS G50401 round ingot,UNS G50401 cold-rolled steel,UNS G50401 coil,UNS G50401 strap steel,UNS G50401 hot-rolled steel,UNS G50401 medium plate, UNS G50401 heavy plate,UNS G50401 shapped bar,UNS G50401 hexahedral bar,UNS G50401,UNS G50401 slab ingot,UNS G50401 slab,UNS G50401 price,UNS G50401 square bar,UNS G50401 square steel,UNS G50401 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS G50401.

Current Location:Home » Products » Alloy steel » UNS G50401

Product category

UNS G50401

Data Table for:Products: Alloy steel:UNS G50401

UNS G50401 properties and heat treatment forged piece, Including UNS G50401 application and specifications, We have all specifications,Including UNS G50401 steel plate, UNS G50401 sheet, UNS G50401 square steel, UNS G50401 flat bar,UNS G50401 round bar,UNS G50401 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS G50401 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS G50401 and Standards

AISI 50B40 steel
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 5000 Series steel; Low Alloy Steel; Carbon Steel; Medium Carbon steel

Key Words: UNI 38 CrB 1 KB (Ital.), medium carbon steels, UNS G50401, ASTM A322, ASTM A519, SAE J404, SAE J412, SAE J770, DIN 1.7007

Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell  174 - 223 174 - 223 annealed and cold drawn.
Hardness, Knoop  221 221 Converted from Brinell hardness.
Hardness, Rockwell B  92 92 Converted from Brinell hardness.
Hardness, Rockwell C  13.0 13.0 Converted from Brinell hardness. Value below normal HRC range, for comparison purposes only.
Hardness, Vickers  208 208 Converted from Brinell hardness.
Modulus of Elasticity  205 GPa 29700 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel.
Poissons Ratio  0.290 0.290 Calculated
Machinability  65 % 65 % annealed and cold drawn. Based on 100% machinability for AISI 1212 steel.
Shear Modulus  80.0 GPa 11600 ksi Typical for steels.
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000219 ohm-cm 0.0000219 ohm-cm Typical 5000 series steel
 
Thermal Properties Metric English Comments
Specific Heat Capacity  0.475 J/g-°C 0.114 BTU/lb-°F Typical 4000 series steel
Thermal Conductivity  46.6 W/m-K 323 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Boron, B  0.000500 - 0.00300 % 0.000500 - 0.00300 %
Carbon, C  0.380 - 0.430 % 0.380 - 0.430 %
Chromium, Cr  0.400 - 0.600 % 0.400 - 0.600 %
Iron, Fe  97.592 - 98.3195 % 97.592 - 98.3195 % As remainder
Manganese, Mn  0.750 - 1.00 % 0.750 - 1.00 %
Phosphorous, P  <= 0.0350 % <= 0.0350 %
Silicon, Si  0.150 - 0.300 % 0.150 - 0.300 %
Sulfur, S  <= 0.0400 % <= 0.0400 %

Users viewing this material also viewed the following:
AISI E50100 Steel
AISI 50B40H Steel
AISI 50B44 Steel
AISI 5046 Steel
Overview of materials for AISI 5000 Series Steel

M504AA / 8029
 




Machining performance

Download UNS G50401 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.