Our to produce better steel-based products are the main used in industrial manufacturing various types Low alloy high-temperature steelUNS H40420 plate,UNS H40420 Round Bar,UNS H40420 forgings,UNS H40420 suppliers, UNS H40420 Stock,UNS H40420 sheet, UNS H40420 flat bar, UNS H40420 pipe,UNS H40420 tube,UNS H40420 mould,UNS H40420 round ingot,UNS H40420 cold-rolled steel,UNS H40420 coil,UNS H40420 strap steel,UNS H40420 hot-rolled steel,UNS H40420 medium plate, UNS H40420 heavy plate,UNS H40420 shapped bar,UNS H40420 hexahedral bar,UNS H40420,UNS H40420 slab ingot,UNS H40420 slab,UNS H40420 price,UNS H40420 square bar,UNS H40420 square steel,UNS H40420 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS H40420.

Current Location:Home » Products » Low alloy high-temperature steel » UNS H40420

Product category

UNS H40420

Data Table for:Products: Low alloy high-temperature steel:UNS H40420

UNS H40420 properties and heat treatment forged piece, Including UNS H40420 application and specifications, We have all specifications,Including UNS H40420 steel plate, UNS H40420 sheet, UNS H40420 square steel, UNS H40420 flat bar,UNS H40420 round bar,UNS H40420 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS H40420 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS H40420 and Standards

AISI 4042H steel
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel; Low Alloy Steel; Carbon Steel; Medium Carbon steel
Material Notes: Oil quenched. Forging temp.: 1230 °C (2250°F) max. Annealing temp.: 830°C - 925°C (max. hardness 183 HB). Normalizing temp.: 855 - 955°C (approx. hardness 235 HB). Hardening temp.: 830 - 855°C
Key Words: Alloy Steels, UNS H40420, ASTM A304, SAE J1268

Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell  179 - 229 179 - 229
Hardness, Knoop  226 226 Converted from Brinell hardness.
Hardness, Rockwell B  93 93 Converted from Brinell hardness.
Hardness, Rockwell C  14.0 14.0 Converted from Brinell hardness. Value below normal HRC range, for comparison purposes only.
Hardness, Vickers  214 214 Converted from Brinell hardness.
Modulus of Elasticity  205 GPa 29700 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Calculated
Machinability  65 % 65 % annealed and cold drawn. Based on 100% machinability for AISI 1212 steel.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000245 ohm-cm 0.0000245 ohm-cm Typical 4000 series steel
 
Thermal Properties Metric English Comments
Specific Heat Capacity  0.475 J/g-°C 0.114 BTU/lb-°F Typical 4000 series steel
Thermal Conductivity  44.5 W/m-K 309 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Carbon, C  0.390 - 0.460 % 0.390 - 0.460 %
Iron, Fe  97.82 - 98.66 % 97.82 - 98.66 % As remainder
Manganese, Mn  0.60 - 1.0 % 0.60 - 1.0 %
Molybdenum, Mo  0.20 - 0.30 % 0.20 - 0.30 %
Phosphorous, P  <= 0.035 % <= 0.035 %
Silicon, Si  0.15 - 0.35 % 0.15 - 0.35 %
Sulfur, S  <= 0.040 % <= 0.040 %

Users viewing this material also viewed the following:
AISI 4042 Steel
AISI 4047H Steel
AISI 4037H Steel
AISI 4037 Steel
AISI 4047 Steel

M4042B / 7458
 




Machining performance

Download UNS H40420 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.