Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyUNS R50400 plate,UNS R50400 Round Bar,UNS R50400 forgings,UNS R50400 suppliers, UNS R50400 Stock,UNS R50400 sheet, UNS R50400 flat bar, UNS R50400 pipe,UNS R50400 tube,UNS R50400 mould,UNS R50400 round ingot,UNS R50400 cold-rolled steel,UNS R50400 coil,UNS R50400 strap steel,UNS R50400 hot-rolled steel,UNS R50400 medium plate, UNS R50400 heavy plate,UNS R50400 shapped bar,UNS R50400 hexahedral bar,UNS R50400,UNS R50400 slab ingot,UNS R50400 slab,UNS R50400 price,UNS R50400 square bar,UNS R50400 square steel,UNS R50400 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS R50400.

Current Location:Home » Products » Ti Alloy » UNS R50400

Product category

UNS R50400

Data Table for:Products: Ti Alloy:UNS R50400

UNS R50400 properties and heat treatment forged piece, Including UNS R50400 application and specifications, We have all specifications,Including UNS R50400 steel plate, UNS R50400 sheet, UNS R50400 square steel, UNS R50400 flat bar,UNS R50400 round bar,UNS R50400 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS R50400 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS R50400 and Standards

Allvac® 40, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Categories: Metal; Nonferrous Metal; Titanium Alloy; Unalloyed/Modified Titanium
Material Notes: Data provided by Allvac.
Applications: Airframe components, cryogenic vessels, heat exchangers, CPI equipment, condenser tubing, pickling baskets.

 

Key Words: UNS R50400; AMS 4902, 4921, 4942; MIL-T-9046, -81556. ASTM F 67, Titanium Grade 2; ASTM B 265, 337, 338, 348; Allvac, an Allegheny Teledyne Company

Physical Properties Metric English Comments
Density  4.51 g/cc 0.163 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Rockwell B  80 80
Tensile Strength, Ultimate  345 MPa 50000 psi
Tensile Strength, Yield  276 MPa
@Strain 0.200 %
40000 psi
@Strain 0.200 %
Elongation at Break  20.0 % 20.0 %
Reduction of Area  30.0 % 30.0 %
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.10 % <= 0.10 %
Hydrogen, H  <= 0.015 % <= 0.015 %
Iron, Fe  <= 0.30 % <= 0.30 %
Nitrogen, N  <= 0.030 % <= 0.030 %
Oxygen, O  <= 0.25 % <= 0.25 %
Titanium, Ti  99.0 % 99.0 % as balance

Users viewing this material also viewed the following:
Allvac® 30, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Allvac® 70, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Allvac® 55, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
Titanium Grade 2, Annealed
Allegheny Ludlum Grade 2 Titanium (UNS R50400)

NALL41 / 14791
 




Machining performance

Download UNS R50400 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.