Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyUNS R58030 plate,UNS R58030 Round Bar,UNS R58030 forgings,UNS R58030 suppliers, UNS R58030 Stock,UNS R58030 sheet, UNS R58030 flat bar, UNS R58030 pipe,UNS R58030 tube,UNS R58030 mould,UNS R58030 round ingot,UNS R58030 cold-rolled steel,UNS R58030 coil,UNS R58030 strap steel,UNS R58030 hot-rolled steel,UNS R58030 medium plate, UNS R58030 heavy plate,UNS R58030 shapped bar,UNS R58030 hexahedral bar,UNS R58030,UNS R58030 slab ingot,UNS R58030 slab,UNS R58030 price,UNS R58030 square bar,UNS R58030 square steel,UNS R58030 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS R58030.

Current Location:Home » Products » Ti Alloy » UNS R58030

Product category

UNS R58030

Data Table for:Products: Ti Alloy:UNS R58030

UNS R58030 properties and heat treatment forged piece, Including UNS R58030 application and specifications, We have all specifications,Including UNS R58030 steel plate, UNS R58030 sheet, UNS R58030 square steel, UNS R58030 flat bar,UNS R58030 round bar,UNS R58030 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS R58030 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS R58030 and Standards

Titanium Beta III (Ti-11.5Mo-6Zr-4.5Sn; Grade 10), Solution Treated, Unaged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Material Notes: 5 other heat treatments of this alloy are in MatWeb.

Key Words: Ti-11.5Mo-6Zr-4.5Sn; UNS R58030; Beta 3

Physical Properties Metric English Comments
Density  5.06 g/cc 0.183 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Vickers  240 240
Tensile Strength, Ultimate  725 MPa 105000 psi
Tensile Strength, Yield  620 MPa 89900 psi
Elongation at Break  15.0 % 15.0 %
Reduction of Area  65.0 % 65.0 %
Modulus of Elasticity  79.0 GPa 11500 ksi
Compressive Yield Strength  800 MPa 116000 psi
Poissons Ratio  0.360 0.360
Fracture Toughness  160 MPa-m½ 146 ksi-in½ K(IC)
Shear Modulus  27.0 GPa 3920 ksi
Shear Strength  590 MPa 85600 psi Ultimate shear strength
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.000156 ohm-cm 0.000156 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 7.60 µm/m-°C
@Temperature 20.0 - 100 °C
4.22 µin/in-°F
@Temperature 68.0 - 212 °F
  8.10 µm/m-°C
@Temperature 20.0 - 315 °C
4.50 µin/in-°F
@Temperature 68.0 - 599 °F
average
  8.70 µm/m-°C
@Temperature 20.0 - 540 °C
4.83 µin/in-°F
@Temperature 68.0 - 1000 °F
average
Specific Heat Capacity  0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity  6.28 W/m-K 43.6 BTU-in/hr-ft²-°F
Melting Point  1573 - 1690 °C 2863 - 3070 °F
Solidus  1573 °C 2863 °F
Liquidus  1690 °C 3070 °F
Beta Transus  760 °C 1400 °F Slow transition kinetics
 
Component Elements Properties Metric English Comments
Molybdenum, Mo  11.5 % 11.5 %
Tin, Sn  4.50 % 4.50 %
Titanium, Ti  78.0 % 78.0 %
Zirconium, Zr  6.0 % 6.0 %

Users viewing this material also viewed the following:
Titanium Beta III (Ti-11.5Mo-6Zr-4.5Sn; Grade 10), ST 720°C, Aged 550°C
Titanium Ti-3Al-2.5V (Grade 9), Alpha-Beta Anneal, Quenched
Titanium Ti-11.5Mo-6Zr-4.5Sn, ST 720°C, Aged 495°C
Titanium Beta C (Ti-3Al-8V-6Cr-4Mo-4Zr) Solution Treated 815°C
Titanium Ti-5-5-2-3 (Ti-5Mo-5V-2Cr-3Al), 12 mm Rod, Aged

MTB030 / 14152
 




Machining performance

Download UNS R58030 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.